Unravelling the anionic stability of an ether-based electrolyte with a hard carbon or metallic sodium anode for high-performance sodium-ion batteries

In hard carbon (HC) anodes, elucidating the relationship between the solid electrolyte interphase formation and the solvated Na + co-intercalation mechanism is crucial, particularly considering different anionic salts in ether-based electrolytes. Here, we comprehensively explore the impact of different anionic salts on the electrochemical performance of HC/Na half-cell and elucidate the underlying mechanism through experimental studies and theoretical calculations. The surface morphology of the HC anode and its interphasial property are further investigated to evaluate the differences endowed by the presence of various anionic salts in diglyme (2G). The HC/Na half-cells with NaPF 6 -2G and sodium trifluoromethanesulfonate (NaCF 3 SO 3 )-2G display superior electrochemical performance with faster kinetics and lower interfacial resistance than those with NaClO 4 -2G, sodium bis-(fluorosulfonyl) imide (NaFSI)-2G and sodium bis-(trifluoromethanesulfonyl) imide (NaTFSI)-2G. NaClO 4 -2G forms a relatively thick interphase layer with high resistance at the electrode/electrolyte interface owing to its insufficient stability. NaFSI-2G and NaTFSI-2G exhibit severe side reactions with Na metal, producing a thick interphase layer on the HC surface with high interfacial resistance from excess electrolyte decomposition, thus deteriorating the electrochemical performance. In summary, the study on the stability of different anionic salts in ether-based electrolyte for the HC anode with the intercalation mechanism provides valuable insights for screening appropriate conductive salts for high-performance sodium-ion batteries, especially when considering Na metal counter/reference electrodes.