Synthesis and performances of a ZnCo2O4@MnMoO4 composite for a hybrid supercapacitor

To overcome the disadvantages of poor intrinsic conductivity and stability of ZnCo2O4, a ZnCo2O4@MnMoO4 composite as an emerging pseudocapacitor electrode material with high specific capacitance, environmental friendliness, morphological diversity, and unique hierarchical structure was synthesized via a simple two-step hydrothermal method. The research results indicate that the ZnCo2O4@MnMoO4 composite can present a high specific capacity of 1628 F g−1 at a current density of 1 A g−1 and good cycling stability with 69% capacity retention after 10 000 cycles at 10 A g−1. Hybrid supercapacitors (HSCs) assembled with the ZnCo2O4@MnMoO4 cathode and activated carbon anode can deliver an energy density of 48 W h kg−1 at a power density of 695 W kg−1, and their capacity retention reached 61% after 8000 charge–discharge cycles at a current density of 10 A g−1. This could be attributed to the synergistic effect of the specific surface area and electrical conductivity enhanced by compositing ZnCo2O4 with MnMoO4. As a result, the excellent electrochemical properties show that the ZnCo2O4@MnMoO4 composite has strong application potential for high-performance supercapacitors.