Structural, morphological, mechanical, and thermal insulation properties of multiple-phase magnesium silicate ceramic fibers electrospun from dual-precursor sols

As the research for advanced materials suitable for high-temperature uses continues, the need for oxide ceramic micro-nanofibers with outstanding mechanical and thermal properties becomes increasingly important. By incorporating two types of magnesium sources, specifically Mg(CH 3 COO) 2 ·4H 2 O and MgCl 2 ·6H 2 O, into the precursor, a range of fibers made of magnesium silicate ceramics was produced through electrospinning. X-ray diffraction (XRD) analysis verified that the resulting multiple phases included MgO , MgSiO 3 , Mg 2 SiO 4 , and amorphous SiO 2 , with the phase composition being affected by the diffusion reaction of Mg ions . The fibers produced using the dual-precursor method maintained a stable morphology with a uniform and compact structure after undergoing high-temperature treatments ranging from 1000 to 1200 °C. This study is the first to report the tensile strength of magnesium silicate fibrous membranes , which was found to be 1.54 ± 0.27 MPa and 1.21 ± 0.73 MPa after heat treatment at 800 °C and 1000 °C, respectively. Furthermore, these fibrous membranes demonstrated dependable thermal insulation properties within the testing range of 500–1000 °C, along with a low thermal conductivity at room temperature of 0.0301–0.0306 W m −1 ·K −1 . Characterized by their impressive mechanical strength and high temperature stability, magnesium silicate ceramic micro-nanofibers show significant potential for various applications in the targeted field.