Preparing of N-P dual-doped auricularia auricula carbon host by yeast fermentation and its application in Li-S batteries

A nitrogen-phosphorus dual-doped auricularia auricula carbon (NP-AC) matrix was prepared through hydrothermal treatment using natural auricularia auricula as raw material and medium solution. Yeast was introduced and cultured by the auricularia auricula liquid medium. The NP-AC/S composite was prepared through further freeze-drying, carbonization, activation and compounding with sulfur procedures. The composition and microstructure of samples was characterized by X-ray diffraction (XRD), raman and X-ray photoelectron spectroscopy (XPS). The morphology was observed under scanning electron microscope (SEM) and transmission electron microscopy (TEM) method. The specific surface area was analyzed using nitrogen adsorption/desorption test. The weight ratio of sulfur was measured through thermogravimetric (TG) analysis. The original structure and composition of biomass were improved by yeast fermentation and the auricularia auricula block structure with low porosity was modified. The electrochemical performance of NP-AC/S composite in Li-S batteries was systematically explored. After 100 cycles at 0.2C current density, there was still nearly 1000 mAh g −1 reversible capacity, holding a capacity retention rate of more than 84 %. The cycle performance and rate performance were both far better than the ordinary activated carbon materials.