In-situ synthesis to promote surface reconstruction of metal–organic frameworks for high-performance water/seawater oxidation

Metal-organic frameworks (MOFs) have gained tremendous notice for the application in alkaline water/seawater oxidation due to their tunable structures and abundant accessible metal sites. However, exploring cost-effective oxygen evolution reaction (OER) electrocatalysts with high catalytic activity and excellent stability remains a great challenge. In this work, a promising strategy is proposed to regulate the crystalline structures and electronic properties of NiFe-metal-organic frameworks (NiFe-MOFs) by altering the organic ligands. As a representative sample, NiFe-BDC (BDC: C 8 H 6 O 4 ) synthesized on nickel foam (NF) shows extraordinary OER activity in alkaline condition, delivering ultralow overpotentials of 204, 234 and 273 mV at 10, 100, and 300 mA cm −2 , respectively, with a small Tafel slope of 21.6 mV dec −1 . Only a slight decrease is observed when operating in alkaline seawater. The potential attenuation is barely identified at 200 mA cm −2 over 200 h continuous test, indicating the remarkable stability and corrosion resistance. In-situ measurements indicate that initial Ni 2+ /Fe 2+ goes through oxidation process into Ni 3+ /Fe 3+ during OER, and eventually presents in the form of NiFeOOH/NiFe-BDC heterojunction. The unique self-reconstructed surface is responsible for the low reaction barrier and fast reaction kinetics. This work provides an effective strategy to develop efficient MOF-based electrocatalysts and an insightful view on the dynamic structural evolution during OER.