Green synthesis and high-performance fluoride ion removal using lanthanum-modulated MOF-808 (Zr)

In a water solution and with a low reaction temperature of 85 °C, the green preparation of lanthanum-modulated MOF-808 (Zr) was realized, the obtained La-MOF-808 have smaller grain size, larger specific surface area, higher pore volume and larger average pore diameter. When the molar ratio of La: Zr=1:1, 1L-MOF-808 had the best fluoride ion removal performance, and its maximum adsorption capacity for F - reached 101.4 mg/g, which was higher than that of the unmodulated MOF-808 and some other reported fluorine adsorbents. Meanwhile, the regeneration experiment demonstrated that even after five cycles, 1L-MOF-808 retained 73.8 % of its initial adsorption capacity, highlighting its commendable reusability. In addition, when 1L-MOF-808 was applied to actual fluorine-containing wastewater, with the fluoride ion concentration of 25.3 mg/L and an adsorbent dosage of 0.6 g/L, 1L-MOF-808 exhibited excellent resistance to anionic interference (SO 4 2- , Cl - ), the concentration of fluoride ions in effluent was lower than 10 mg/L, meeting the stipulations of fluoride ion discharge outlined in GB39371–2020. Further adsorption mechanism investigation revealed that 1L-MOF-808's affinity for F - was attributed to electrostatic interaction and ligand exchange. Overall, the as-synthesized 1L-MOF-808 not only presents an environmentally friendly approach to producing MOF materials without organic solvents but also develops a new strategy for the design of high-performance adsorbent for effectively removing fluoride ions from wastewater.