Fabrication of hollow fiber composite membranes via opposite transmission reaction method for dye/salt separation

The separation layer prepared by the conventional coating-crosslinking method is typically thick and prone to forming defective macropores , significantly affecting the water permeability and dye/salt separation performance of membranes. This work presented a novel method to prepare hollow fiber composite membranes for dye/salt separation based on the opposite transmission reaction of crosslinker . In this method, the macromolecule in situ reacted with a small‐molecule crosslinker at the openings of membrane pore channels, forming a separation layer with discontinuous sheet-like and granular structure. Compared to the conventional forward coating-crosslinking method, the separation layer prepared by the opposite transmission reaction method exhibited an ultra-thin thickness of 29.1 nm. Consequently, the composite membrane exhibited a high water permeability of 72.7 L·m −2 ·h −1 ·bar −1 , which was 2.3 times higher than that of conventional methods. Moreover, the prepared composite membrane presented a more uniformed pore structure , completely retaining the VBB (100%) with a low Na 2 SO 4 rejection of 4.3%, demonstrating excellent dye/salt separation performance. Additionally, the prepared composite membrane exhibited superior anti-fouling properties compared to that prepared by the conventional method. Therefore, the opposite transmission reaction method proposed in this study held promising applications in the preparation of hollow fiber composite membranes for efficient dye/salt separation.