Capacitive-Controlled Prussian White with a Nickel Iron Hexacyanoferrate Composite Cathode for Rapid Sodium Diffusion

Prussian blue analogues receive tremendous attention owing to their spacious three-dimensional skeleton, high theoretical specific capacity, facile synthesis procedure, and high cost-effectiveness as among the most promising candidates for cathode materials in sodium-ion batteries (SIBs). Nonetheless, the practical specific capacity, especially under high current, is particularly frail due to the sluggish ion diffusion. In this study, the strategy of Ni substitution and formation of water-coordinated Fe is applied to lower the crystal field energy and elevate the active low-spin (LS) Fe content, which leads to a capacitive sodium storage mechanism, resulting in a substantial specific capacity under high current density. The delivered specific capacity of PW-325@2NiFe-55 is 95 mAh g–1 at 50 C, which is 72.5% capacity retention of the one at 0.5 C. Also, it maintains 80.2% of its initial specific capacity after 500 cycles at 5 C. Furthermore, a hypothesis of a joint diffusion-controlled and capacitive mechanism for high-spin (HS) Fe and a mere capacitive mechanism for LS Fe is put forward and verified through potentiastatic tests, operando 57Fe Mössbauer spectroscopy, and ex situ XRD, which provides a new horizon to enhance the electrochemical performance for SIBs.