Microwave dielectric properties of glass-free CaMg0.9-xLi0.2ZnxSi2O6 ceramics for LTCC applications
CERAMICS INTERNATIONAL [2020]
Fangyi Huang, Hua Su, Yulan Jing, Yuanxun Li, Qihai Lu, Xiaoli Tang