Lattice-tailored low-temperature processed electron transporting materials boost the open-circuit voltage of planar CsPbBr3 perovskite solar cells up to 1.654 V

Journal of Materials Chemistry A [2020]
Yafeng Xu, Jialong Duan, Xiya Yang, Jian Du, Yudi Wang, Yanyan Duan, Qunwei Tang