Synthesis and properties of blue zirconia ceramic based on Ni/Co doped Ba0.956Mg0.912Al10.088O17 blue pigments

Novel blue pigments based on Ba 0.956 Mg 0.912 Al 10.088- x Ni x O 17 (0 ≤  x  ≤ 0.3) and Ba 0.956 Mg 0.912 Al 10.088- x Co x O 17 (0 ≤  x  ≤ 0.3) solid solutions were successfully synthesized by solid state method. The XRD results confirmed the structure of the as-synthesized sample belongs to hexagonal β -alumina structure with the space group of P 6 3 / mmc. The d-d electron transitions in Ni 2+ /Co 2+ tetrahedral sites in the visible light range are the reason for the blue colors. Then, the as-prepared blue oxides were sintered with ZrO 2 powders at 1400 °C to prepare blue zirconia ceramic materials. Based on XRD and SEM analysis, the pigment phase is stable after high-temperature sintering with ZrO 2 , and a clear grain boundary is observed. The XCT results indicate the prepared blue ceramics are dense and very small pores are rarely distributed inside the blue zirconia ceramic body. Additionally, the mechanical properties of the fabricated blue ceramics were maintained compared to pure ZrO 2 ceramic.