Preparation of boronic acid and carboxyl-modified molecularly imprinted polymer and application in a novel chromatography mediated hollow fiber membrane to selectively extract glucose from cellulose hydrolysis

A novel boronic acid and carboxyl-modified glucose molecularly imprinted polymer were prepared through suspension polymerization, which is based on 1.0 mmol glucose as a template, 1.2 mmol methacrylamidophenylboronic acid, and 6.8 mmol methacrylic acids as monomers, 19 mmol ethyleneglycol dimethacrylate, and 1 mmol methylene-bis-acrylamide as crosslinkers. The prepared glucose-molecularly imprinted polymer had a particle size of 25–70 μm, and was thermally stable below 215°C, with a specific surface area of 174.82 m 2/ g and average pore size of 9.48 nm. The best selectivity between glucose and fructose was 2.71 and the maximum adsorption capacity of glucose- molecularly imprinted polymer was up to 236.32 mg / g which was consistent with the Langmuir adsorption model. The similar adsorption abilities in six successive runs and the good desorption rate (99.4%) verified glucose-molecularly imprinted polymer could be reused. It was successfully used for extracting glucose from cellulose hydrolysis. The adsorption amount of glucose was 2.61 mg/mL and selectivity between glucose and xylose reached 4.12. A newly established chromatography (glucose-molecularly imprinted polymer) mediated hollow fiber membrane method in time separated pure glucose from cellulose hydrolysates on a large scale, and purified glucose solution with a concentration of 3.84 mg/mL was obtained, which offered a feasible way for the industrial production of glucose from cellulose hydrolysates.