Heterogeneous catalytic oxidation of tetracycline hydrochloride based on persulfate activated by Fe3O4/MC composite

In this study, a novel magnetic mesoporous carbon composite (Fe 3 O 4 /MC) was prepared by manganese carbonate (MnCO 3 ) as the template to activate persulfate (PS) for tetracycline hydrochloride (TC) degradation. The characterization results showed that Fe 3 O 4 nanoparticles were evenly distributed on the surface of MC, and Fe 3 O 4 /MC had the large surface area of 433.88 m 2 ∙g −1 . When the initial TC concentration was 50 mg·L −1 , Fe 3 O 4 /MC dosage was 0.0336 g, PS dosage was 0.0476 g and the reaction temperature was 30 °C, Fe 3 O 4 /MC + PS system could degrade 92.9% of TC within 90 min. TC degradation efficiency increased with the increase of Fe 3 O 4 /MC dosage and temperature, but decreased with the increase of TC initial concentration and pH value. The increase of PS concentration first improved TC degradation efficiency, and then was not conducive to its degradation. The quenching experiments indicated that the sulfate radical (SO 4 •− ), superoxide radical (•O 2 – ) and singlet oxygen ( 1 O 2 ) in Fe 3 O 4 /MC + PS system contributed to TC degradation. Meanwhile, the toxicity evaluation of the degradation products confirmed that the toxicity of TC in Fe 3 O 4 /MC + PS system was greatly reduced. Totally, this study systematically investigated the performance of the Fe 3 O 4 /MC + PS system for TC removal, laying a theoretical and practical foundation for treatment of potential antibiotic wastewater (ppm range) in the future.