D-Cysteine Functionalized Superhydrophobic Nanocomposite Coating with Multiple-Action Antibacterial Property and Enhanced Mechanical Durability

In this study, a durable superhydrophobic antibacterial coating was developed by a facile spraying method. A mixture of bisphenol A diglycidyl ether (BADGE) and hydrophobic SiO2nanoparticles was sprayed on carbon steel to provide a superhydrophobic substrate. D-cysteine (D-cys) functionalized SiO2/dopamine/silver nanoparticles with multilayer core-shell structure were then sprayed on superhydrophobic substrate to enhance antibacterial performance. The results of morphology observation and X-ray photoelectron spectroscopy (XPS) indicated the successful preparation of antibacterial nanoparticles and presented the hierarchical micro/nanostructures of coating surface. The as-prepared coating exhibited superhydrophobicity, with the water contact angle of ~153°. The coating was endowed with good mechanical durability, which maintained the water contact angle of ~150° after 180 cycles in tape-peel tests. The results of electrochemical impedance spectroscopy showed satisfactory corrosion resistance of this coating during 3 days of immersion in 3.5% NaCl solution. Furthermore, the coating showed excellent antibacterial performances againstEscherichia coliandPseudomonas aeruginosa, which benefited from the synergistic actions of low wettability of superhydrophobic surface, bactericidal behavior of Ag nanoparticles, and biofilm inhibition effect of D-cys.Keywords:superhydrophobic coatings;antibacterial;D-cysteine;silver nanoparticles