Self-assembly of hierarchical MXene@SnO2 nanostructure for enhancing the flame retardancy, solar de-icing, and mechanical property of polyurethane resin

Taking into consideration the frigid and thunderstorms, the flame retardancy and de-icing performance are simultaneously desiderated for some open-air key equipment, such as air fuselage and wind turbine blades. Here, inspired by the anti-reflection phenomenon of moth eyes and cicada wings, a multi-functionalized and biomimetic MXene@SnO 2 hierarchical nanostructure is prepared to effectively impart flame retardancy and solar de-icing performance to thermoplastic polyurethane (TPU) resin used widely as the finishing coat of protective materials of open-air equipment. Based on the catalytic effect and barrier function, the addition of hierarchical MXene@SnO 2 nanostructures also effectively decreases the release of heat and toxic smoke from PU resin, as confirmed by reductions of 50.5% and 33.1% in the peak heat release rate and smoke production rate, respectively. Due to the appropriate refractive index , the light reflection phenomenon is effectively suppressed, thus promoting solar absorption (∼90% at 0.4 mm film) and photo-thermal conversion (∼74.2 °C with simulated solar illumination of 1.0 kW/m 2 ) in TPU-MXene@SnO 2 nanocomposites . Within the environment of −20 °C, the surface temperature of TPU-MXene@SnO 2 nanocomposites is still up to 32.7 °C and the surface ice pellet begins to melt at ∼40s, much earlier than 600s of pure TPU resin. In addition, the practical application of functionalized TPU nanocomposites is further improved by the higher mechanical properties , attributed to the strong interfacial interaction . Inspired by moth eyes and cicada wings, flame retardancy and solar de-icing performance are first integrated into polymer materials, thus effectively promoting their application in some extreme environments.