In situ growth of UiO-66-NH2 in wood-derived cellulose for iodine adsorption

The capture of radioactive iodine is an inevitable requirement in nuclear industry for environmental protection. Metal-organic frameworks (MOFs) are a new generation of sorbents that have wide applications for iodine adsorption and recovery. Although the loading of MOFs on wood can avoid the drawbacks of the powder form of MOFs in implementation, the dense structure of wood results in the lower loading, even after delignification, which limits the adsorption capacity. Herein, a hierarchically porous UiO-66-NH 2 @WCA composite was fabricated by in-situ synthesis of UiO-66-NH 2 in wood-derived cellulose aerogel (WCA) that was further removed hemicellulose from delignified wood. UiO-66-NH 2 @WCA exhibited a high loading (36 wt%) of UiO-66-NH 2 crystals and a high adsorption capacity of 704 mg/g for iodine vapor and 248 mg/g for iodine aqueous solution. The adsorption behavior in iodine aqueous solution was well predicted by the Freundlich isotherm and pseudo-second-order kinetic model. The adsorption capacity of UiO-66-NH 2 @WCA was highest in solution when the pH was 6, while the ionic strength had little effect. The hydroxyl groups on the WCA matrix had a charge transfer effect with iodine, providing additional sites for iodine capture . Furthermore, a packed column system was applied to demonstrate the excellent recyclability and potential for practical application.