Efficient degradation of phenol by MnOOH-rGO composite with high peroxymonosulfate utilization efficiency

A high-performance, durable, low-cost, and environmentally friendly catalyst is highly desired in advanced oxidation processes (AOPs) for water treatment . Considering the activity of Mn(Ⅲ) and the superior catalytic properties of reduced graphene oxide (rGO) in peroxymonosulfate (PMS) activation, rGO-modified MnOOH nanowires (MnOOH-rGO) were fabricated by a hydrothermal method for phenol degradation. The results showed that the composite synthesized at 120 °C with 1 wt% rGO dopant exhibited the best performance for phenol degradation. Nearly 100% of the phenol was removed by MnOOH-rGO within 30 min, which is higher than the removal rate of pure MnOOH (70%). The effects of catalyst dosages, PMS concentration, pH, temperature, and anions (Cl − , NO 3 − , HPO 4 2− and HCO 3 − ) on phenol degradation were investigated. The removal rate of chemical oxygen demand (COD) reached 26.4%, with a low molar ratio of PMS to phenol at 5:1 and a high PMS utilization efficiency (PUE) of 88.8%. The phenol removal rate remained more than 90% after five recycle with less than 0.1 mg L −1 leakage of manganese ions . Together with the results of radical quenching experiments, X-ray photoelectron spectroscopy (XPS) and electron paramagnetic resonance spectroscopy (EPR), electron transfer and 1 O 2 were proved to dominate the activation process. During the direct electrons transfer process, the electrons transfer from the phenol to PMS by using the Mn(Ⅲ) as the mediate with a stoichiometric ratio between PMS and phenol at 1:2, which mainly contributed to the high PUE. This work provides new insight into a high-performance Mn(Ⅲ) based catalyst on PMS activation with high PUE, good reusability, and environmentally friendly for removing organic pollutants.