A multiple cross-linking strategy to develop an environment-friendly and water resistance wheat gluten protein wood adhesive

Wheat gluten (WG) shows great promise to synthesize environment-friendly wood adhesives. However, their weak bonding strength and poor water resistance have limited its application in the commercial wood-based panel industry. In this study, a novel WG-based adhesive was developed by constructing a multiple cross-linking network generated by covalent and non-covalent bonds. The potential mechanism was revealed by FT-IR analysis. Furthermore, their surface morphology, thermal stability , viscosity, and residual rate of adhesives with different compositions were systematically characterized and compared. The results showed that the hydrogen bonding, reactions between amine groups and tannin , and ring opening reaction of epoxy, synergistically contributed to generate a highly crosslinked network. The wet/boil water strength of the plywood prepared from WG/tannin/ethylene imine polymer (PEI)-glycerol triglycidyl ether (GTE) adhesive with the addition of 15 % GTE could reach 1.21 MPa and 1.20 MPa, respectively, and a mildew resistance ability was observed. This study provides a facile strategy to fabricate high-performance plant protein-based adhesives with desirable water resistance for practical application.