Self-adhesive wearable poly (vinyl alcohol)-based hybrid biofuel cell powered by human bio-fluids

Advancement of wearable microelectronics demands their power source with continuous energy supply, skin-integration and miniaturization. In light of poly (vinyl alcohol) (PVA) hydrogel with nontoxicity, good biocompatibility and low cost, an advanced wearable PVA-based hybrid biofuel cells (HBFCs) with high self-adhesiveness was developed. Through the reaction between PVA molecules and succinic anhydride (SAA), the carboxylated PVA (PVA/SAA) was obtained, and by incorporation with PDA as crosslinker , the self-adhesive PVA/SAA-DA hydrogel electrolytes formed by dual covalent and hydrogen bonding . With increasing SAA and PDA content, the pore size decreased, and a uniform and dense network formed, endowing the hydrogel with a relatively high absorption capacity of PBS solution of lactate as cell fuel. Meanwhile the various functional groups of hydrogel, including catechol , quinone , amino and hydroxyl groups , contributed to impressive tissue adhesion strength against pigskin under dry and wet conditions. The PVA/SAA-DA hydrogel displayed high conductive property, and the integrated PVA-based HBFC generated open circuit voltage of 0.50 V and maximum power density of 128.76 μW/cm 2 in 20 mM lactate solution, which was optimized to be 0.57 V/224.85 μW/cm 2 when the pore size was enlarged. The power retention reached above 70% in one week, showing long-term stability of HBFC. The PVA-based HBFC was further adhered to human skin without extra adhesive tapes to scavenge human sweat as biofuel, and the maximum power density reached 85.34 μW/cm 2 , while by connected with a DC-DC converter, the HBFC could power watch, exhibiting promising application potentials as wearable electronic device to provide bioelectricity .