High-performance aqueous rechargeable NiCo//Zn battery with molybdate anion intercalated CoNi-LDH@CP bilayered cathode

Seeking cathode materials with high areal capacity and excellent cycling tolerance is a key step to develop aqueous rechargeable zinc-based alkaline batteries with high energy density, power density and excellent stability. Here, the bilayered cathode composite (MCN-LDH@CP) of molybdate intercalated cobalt–nickel layered hydroxide nanosheets (MCN-LDH) grown on cobalt phosphate octahydrate microsheet (CP) was prepared by a two-step hydrothermal process. Molybdate intercalation significantly reduces the thickness of cobalt–nickel layered hydroxide, greatly increases its specific surface area, regulates its pore distribution, increases the crystal plane spacing, promotes the diffusion rate of hydroxide in it, and increases its specific capacity. Meanwhile, the bilayered MCN-LDH@CP electrode significantly improved the areal energy density (2.89 mWh/cm 2 ) and peak power density (111.22 mW/cm 2 ) and cycle stability (97.8 % after 7000 cycles) of the CoNi//Zn battery. The excellent stability is mainly due to the fact that the MCN-LDH overlay inhibits the loss of P element of CP and improves the structural stability of the sample. The quasi-solid-state MCN-LDH@CP//Zn battery can still charge a mobile phone even when hammered and pierced, showing excellent safety and reliability. This work opens a new avenue to develop CoNi//Zn batteries with high energy density, power density and excellent tolerance.