MXene nanosheets coated conjugated microporous polymers hollow microspheres incorporating with phase change material for continuous desalination

The inevitable intermittency of solar illumination during the interfacial evaporation process can cause a reduction in the evaporation performance of solar evaporators. Here, we report the fabrication of a new solar-driven interfacial evaporator using MXene nanosheets as the photothermal layer, modifying them with conjugated microporous polymer hollow microspheres , and then compounding them with the phase change material , in this case, cetyl alcohol, to form a composite evaporator (CE) that can perform all-weather solar interfacial evaporation. By combining interfacial evaporation photothermal conversion with energy storage, the evaporator achieves an evaporation rate of 1.57 kg⋅m −2 ⋅h −1 at a light intensity of 1 kW⋅m −2 and 2.79 kg⋅m −2 ⋅h −1 at a light intensity of 2 kW⋅m −2 . In addition, the evaporator attains an excellent solar evaporation efficiency of over 91% in both cases and even in salt water. In addition, interestingly, our CE exhibits excellent continuous evaporation ability, e.g., the mass of evaporated water was increased by 0.36 kg⋅m −2 at a light intensity of 2 kW⋅m −2 compared to the cavity evaporator without the phase change material (PCM) when solar light was turned off. These results could be attributed to the fact that the energy released by the incorporated phase change material allows the evaporator to maintain stable evaporation under conditions of insufficient or intermittent solar irradiation, potentially providing a new opportunity for addressing the intermittent problem of evaporation at the solar interface due to unstable light intensity, thus showing great potential for practical continuous desalination .